The influence on physical propertie s of recasting

　　cobalt-chromium alloy in air enviroment.

Zhu Shong，Yu Dezhen， Zhao Hua．

　　College of Stomatology，Norman Bethune University of Medical Sciences，Changchun 130041

　　Abstract Objective：To investigate the effect of recasting on physical properties of a cobalt-chromium alloy in air environment．Methods：To analysis the physical properties include tensile strength，elongation and hardness of each generational samples comparing the metallographic evaluation of porosity defects，non-metal inclusions，grain structure and changed composition．Results：A statistical comparsion was made between the elongation of the first generation and the third generation and it showed a significant difference．Conclusion： It indicates that the cobalt-chromium alloy recasted in air can be reused for at most two generations without the addition of any new alloy，otherwise it would affect the quality of restorations．

　　Key words cobalt-chromium alloy recast physical properties

　　钴铬合金在口腔修复领域应用广泛，为节省材料，降低修复体的成本，有些学者研究铸造剩余合金的回收再利用［1,2］。他们对此问题的研究，多着眼于合金宏观物 理机械性能的改变，而对合金的显微组织研究不足，缺少合金反复铸造后化学成分改变的测试。因而不能阐明钴铬合金的晶粒结构，化学成分等变化与相应的机械性能改变之间的内在联系，更加深入地解释机械性能变化的机理。本实验在前人研究的基础上丰富了检测指标，可为临床工作中正确合理地使用铸造剩余合金提供一些参考依据。

　　材料与方法

　　一、制备拉伸试样

　　制造一套带有栓道的上下二瓣金属阴模模具，上有4个大小相同的对应半个试样的阴模，阴模腔的尺寸如附图。腔内充填调好的自凝塑料，按栓道方向将二瓣模具合为一体，置压盒器上缓慢加压，多余的自凝塑料从排溢孔排出。30分钟后，取出塑料试样，磨光，放入120 ℃的蜂蜡液中浸泡约0.5分钟。将这些塑料试样按常规方法包埋铸造成金属试样。所用铸造 机为日本产Spacetron　Model　TMC-103高频离心铸造机，合金材料 为上海齿科材料厂生产的硬质钴铬合金。铸造的试样每代各保留5个，其余的继续熔铸下一 代。

　　附图　拉伸试样阴模腔示意图(单位：mm)

　　二、试样的检测

　　1. 拉伸实验：用千分尺测出试样拉伸部分的直径，取数值在2.40mm±0.02mm范 围内。表面光滑无划痕的试样。测定试样的标距L0。将上述数值输入日本产AG-10TA 电子万能试验机内的计算机，拉伸速度为1mm／min，试样断裂处位于标距内的为有效，重新对好，测量新的标距L1，伸长率＝(L1-L0)／L0×100％，计算机 可输出试样的抗拉强度。

　　2. 硬度测试：采用维氏硬度计测试。

　　3. 金相观察：常规方法制备试样的金相组织磨片，置于日本Nikon　AFX-Ⅱ 型金相显微镜下观察内部的气孔及非金属性夹杂物，合金晶粒的大小、形态。

　　4. 化学成分分析：切取拉断试样的中心部分，每个样品取两点，通过SEM/EDX方法检测成分，即用日本JXA-840扫描电镜，配置英国LINK-860型X-射线能谱仪进行合金元素的 定性、定量分析。工作电压20KV；束流200MA；收集时间100秒；观察倍数200倍。